OEM Supply Direct Aluminum Wire Scrap – Silver Alloy Wires – ZHJ
China OEM Supply Direct Aluminum Wire Scrap - Silver Alloy Wires - ZHJ Manufacturer and Supplier | ZHJ Detail:
| Application: |
| Contactors, circuit breakers, thermostats, intelligent switches, etc |
| The Material: |
| Ag/FAg,AgNi,AgCdO,AgZnO,AgSnO2,AgSnO2In2O3 |
Microstructure
General Description
Silver and fine grain silver (FAg) possess very high electrical and thermal conductivity, low and stable contact resistance, and good workability. For silver resistance to arc erosion and contact welding are limited, mechanical strength is low, Due to the small quantity of nickel in the fine grain silver, resistance to arc erosion and mechanical strength are higher than that of silver.
Application Scope
Widely used in low current devices, such as relays, timers, auxiliary switches for household appliances , control switches, etc.
Material Properties
|
Ag |
FAg |
|||
|
Tips |
Wires |
Tips |
Wires |
|
| Ag Content (wt.%) |
≥99.95 |
≥99.95 |
99.85 |
99.85 |
| Density (g/cm3) |
≥10.48 |
≥10.48 |
≥10.40 |
≥10.40 |
| Elec. Resistivity (pQ•cnn) |
≤2.10 |
≥1.80 |
≥2.10 |
≥1.85 |
| Hardness HV |
≥40 |
≥60 |
≥45 |
≥65 |
| Tensile Strength (MPa) |
230-380 |
250-380 |
||
| Elongation (%) |
2-30 |
2-30 |
||
| Manufacturing process | Extruding-Rolling | Extruding -Drawing | Extruding-Rolling | Extruding -Drawing |
Product Types
Microstructure
General Description
AgNi materials have higher resistance to arc erosion and contact welding than Ag or FAg. Both properties are improved with increasing Ni content. All AgNi materials show good workability and are easy to weld to contact supports. Low tendency towards material transfer in DC applications. AgNi materials are environment-protective materials.
Application Scope
AgNi contact materials find a wide range of application in low voltage switching devices. They are used in relays, small contactors, light switches, temperature controllers as well as in protective switches (they are used in asymmetric contact pairs, for instance, againstAgC, AgZnO orAgSnO2 materials).
Material Properties
| Wires |
AgNi |
AgNi |
AgNi |
Ag Ni |
AgN i |
AgNi |
| Ni Content (wt.%) |
10±1 |
12±1 |
15±1 |
15±1 |
20±1 |
30±1 |
| Density (g/cm3) |
≥10.25 |
≥10.20 |
≥10.15 |
≥10.15 |
≥10.05 |
≥9.80 |
| Elec.Resistivity (pC2•cm) |
≤1.95 |
≤2.05 |
≤2.05 |
≤2.10 |
≤2.15 |
≤2.50 |
| Hardness HV |
≥75 |
≥70 |
≥80 |
≥80 |
≥80 |
≥80 |
| Tensile Strength (MPa) |
240-450 |
240-450 |
250-360 |
280-460 |
260-380 |
260-380 |
| Elongation(%) |
5-30 |
5-30 |
5-30 |
5-28 |
2-28 |
2-25 |
| Manufacturing process |
Sintering-Extruding |
|||||
Product Types
Microstructure
General Description
AgCdO contacts belong to the group of the most widely used ones on the field of low voltage electric apparatus. They combine a satisfactory resistance against contact welding with a good arc erosion resistance and a fairly low contact resistance over its complete service life. They are produced with two different techniques, pre-oxidation-sintering-extruding and internal oxidation. In both cases Cd0 content may range from 10 to 20wt.%.However,Cd and Cd0 are considered to be hazardous to health and the environment. For this reason the use ofAgCdO materials will be banned in a number of countries.
Application Scope
Mainly used in almost every type of low voltage switching devices. They are typically used in microswitches, relays, light switches, contactors, switches for household appliances, some types of protective switches, as well as in certain types of circuit breakers.
Material Properties
| Wires | AgCdO | AgCdO | AgCdO | AgCdO | AgCdO | AqCd0 | AgCdO |
| CdO Content(wt.%) | 10±1 | 13.5±1 | 15±1 | 10±1 | 12±1 | 15±1 | 17±1 |
| Density (g/cm3) | ≥10.05 | ≥9.95 | ≥9.90 | ≥10.10 | ≥10.05 | ≥9.95 | ≥9.80 |
| Elec.Resistivity (1.10•cm) | ≤2.25 | ≤2.35 | ≤2.40 | ≤2.10 | ≤2.15 | ≤2.25 | ≤2.40 |
| Hardness HV | ≥70 | ≥75 | ≥75 | ≥70 | ≥70 | ≥75 | ≥75 |
| Tensile Strength (MPa) | 260-350 | 260-380 | 260-380 | 260-350 | 260-380 | 260-380 | 260-400 |
| Elongation(%) | 6-20 | 6-20 | 6-20 | 8-25 | 8-25 | 8-25 | 5-25 |
| Manufacturing process | Pre-oxidation-Sintering-Extruding | Internal Oxidation | |||||
Product Types
Microstructure
General Description
A high resistance against contact welding characterizes AgZnO materials. They also show a good resistance against arc erosion. Contact resistance of AgZnO tends to be higher than that of AgCd0. AgZnO can be produced by means of pre-oxidation-sintering —extruding, mixing-compacting-sintering techniques as well as by internal oxidation. AgZnO materials are environment -protective materials.
Application Scope
Mainly used in circuit breakers, especially in universal circuit breakers. Other fields of application are motor protective switches, residual current circuit breakers and AC relays.
Material Properties
|
Wires |
AgZnO |
AgZnO |
| ZnO Content(wt.%) |
8±1 |
10±1 |
| Density (g/cm3) |
.9.65 |
9.60 |
| Elec.Resistivity (NO•cm) |
2.25 |
2.35 |
| Hardness HV |
E30 |
85 |
| Tensile Strength (MPa) | 285-350 |
285-350 |
| Elongation(%) |
15-25 |
12-20 |
| Manufacturing process |
Pre-oxidation -Sintering-Extruding |
|
Product Types
Microstructure
General Description
AgSnO2/AgSn021n203 are eco-friendly electrical contact materials. They have good performances in anti-erosion and anti-welding properties, and have good anti-material transfer property in DC switching circuit. The main manufacturing processes are internal oxidation process, pre-oxidation process, powder metallurgy process, chemical coating process, etc.
Application Scope
Widely used in various kinds of contactors , relays, circuit breakers and switches, etc.
Material Properties
AgSnO2
|
Wires |
AgSnO2 |
AgSnO2 |
AgSnO2 |
AgSnO2 |
AgSn02 |
| SnO2 Content (wt.%) |
10±1 |
10±1 |
12±1 |
12±1 |
15±1 |
| Density (g/cm3) |
≥9.90 |
≥9.95 |
≥9.85 |
≥9.85 |
≥9.5 |
| Elec. Resistivity (pO•cm) |
≤2.15 |
≤2.30 |
≤2.30 |
≤2.30 |
≤2.81 |
| Hardness HV |
≥85 |
≥95 |
≥70 |
≥75 |
≥85 |
| Tensile Strength (MPa) |
295-350 |
290-385 |
230-350 |
230-285 |
250-330 |
| Elongation(%) |
15-25 |
15-25 |
15-25 |
18-30 |
15-25 |
| Manufacturing process |
Pre-oxidation-Sintering-Extruding |
Chemical Coating |
Mixing-Sintering-Extruding |
||
AgSnO2In203
|
Wires |
AgSnO2 |
AgSnO2 |
AgSnO2 |
AgSnO2 |
AgSnO2 |
| Ag Content (wt.%) |
90±1 |
88±1 |
92±1 |
88±1 |
85.5±1 |
| Density (g/cm3) |
≥9.95 |
≥9.95 |
≥9.96 |
≥9.91 |
≥9.72 |
| Elec. Resistivity (10•cm) |
≤2.38 |
≤2.45 |
≤2.25 |
≤2.35 |
≤2.55 |
| Hardness HV |
≥100 |
≥100 |
≥90 |
≥95 |
≥95 |
| Tensile Strength (MPa) |
320-450 |
320-450 |
320-450 |
320-450 |
320-450 |
| Elongation(%) |
15-25 |
15-25 |
18-30 |
18-30 |
18-30 |
| Manufacturing process |
Pre-oxidation-Sintering-Extruding |
Internal Oxidation |
|||
Product Types
Microstructure
General Description
AgSnO2lAgSn021n203 are eco-friendly electrical contact materials. They have good performances in anti-erosion and anti-welding properties, and have good anti-material transfer property in DC switching circuit. The main manufacturing processes are internal oxidation process, pre-oxidation process, powder metallurgy process, chemical coating process, etc.
Application Scope
Widely used in various kinds of contactors , relays, circuit breakers and switches, etc.
Material Properties
AgSnO2
|
Wires |
AgSnO2 |
AgSnO2 |
AgSnO2 |
AgSnO2 |
AgSn02 |
| SnO2 Content (wt.%) |
10 ±1 |
10 ±1 |
12±1 |
12±1 |
15 ±1 |
| Density (g/cm3) |
≥9.90 |
≥9.95 |
≥9.85 |
≥9.85 |
≥9.5 |
| Elec. Resistivity (p0•cm) |
≤2.15 |
≤2.30 |
≤2.30 |
≤2.30 |
≤2.81 |
| Hardness HV |
≥85 |
≥95 |
≥70 |
≥75 |
≥85 |
| Tensile Strength (MPa) |
295-350 |
290-385 |
230-350 |
230-285 |
250-330 |
| Elongation(%) |
15-25 |
15-25 |
15-25 |
18-30 |
15-25 |
| Manufacturing process |
Pre-oxidation-Sintering-Extruding |
Chemical Coating |
Mixing-Sintering-Extruding |
||
AgSnO2In203
|
Wires |
AgSnO2 |
AgSnO2 |
AgSnO2 |
AgSnO2 |
AgSnO2 |
| Ag Content (wt.%) |
90±1 |
88±1 |
92±1 |
88±1 |
85.5±1 |
| Density (g/cm3) |
≥9.95 |
≥9.95 |
≥9.96 |
≥9.91 |
≥9.72 |
| Elec. Resistivity (p0•cm) |
≤2.38 |
≤2.45 |
≤2.25 |
≤2.35 |
≤2.55 |
| Hardness HV |
≥100 |
≥100 |
≥90 |
≥95 |
≥95 |
| Tensile Strength (MPa) |
320-450 |
320-450 |
320-450 |
320-450 |
320-450 |
| Elongation(%) |
15-25 |
15-25 |
18-30 |
18-30 |
18-30 |
| Manufacturing process |
Pre-oxidation-Sintering-Extruding |
Internal Oxidation |
|||
Product Types
Product detail pictures:
Related Product Guide:
Fast and fantastic quotations, informed advisers to help you choose the correct products that suits all your needs, a short manufacturing time, responsible good quality control and distinct companies for paying and shipping affairs for China OEM Supply Direct Aluminum Wire Scrap - Silver Alloy Wires - ZHJ Manufacturer and Supplier | ZHJ , The product will supply to all over the world, such as: Czech republic , Canada , New Delhi , "Good quality, Good service " is always our tenet and credo. We take every effort to control the quality, package, labels etc and our QC will check every detail during producing and before shipment. We are willing to establish long business relationship with those who seek the high quality products and good service. We have set up a wide sales network across European countries, North of America, South of America, Middle East, Africa, East Asia countries.Please contact us now, you will find our professional experience and high quality grades will contribute to your business.
By Gustave
from Poland
- 2018.09.23 17:37
Adhering to the business principle of mutual benefits, we have a happy and successful transaction, we think we will be the best business partner.
By Audrey
from Suriname
- 2018.06.09 12:42