Tukwici na Tuntuɓar Wutar Lantarki
Siffofin samfur:
Azurfa cadmium oxide lantarki lamba abu ne yadu amfani, da low narkewa batu na lamba a cikin lambobi na sublimation iya sa sanyaya surface na lamba, kuma a lokaci guda quenching sakamako, hana lamba kona.
AgSnO2, AgSnO2In2O3 lamba yana da abũbuwan amfãni daga high taurin, high juriya ga Fusion waldi da juriya ga kona da dai sauransu.
Kayan abu shine mafi kyawun kayan kare muhalli don maye gurbin AgCdO.
| Aikace-aikace: |
| Masu tuntuɓar sadarwa, masu watsewar da'ira, ma'aunin zafi da sanyio, masu sauyawa masu hankali, da sauransu |
| Kayan: |
| AgZnO, AgSnO2, AgCu , AgCuO , AgCdO , AgNi , AgSnO2A ciki2O3, AgSnO2/Cu, AgCdO/Cu da dai sauransu. |
| matar aure | Wt% | G/cm3 | μΩ.cm | Mpa | % | HV: KGF/MM2 |
| AgCdO10 | 90 | ≥ 10.1 | ≤2.10 | ≥260 | ≥15 | ≥50 |
| AgCdO10 | 88 | ≥ 10.0 | ≤2.2 | ≥260 | ≥12 | ≥60 |
| AgCdO10 | 85 | ≥9.85 | ≤2.3 | ≥260 | ≥10 | ≥65 |
| AgCdO10 | 83 | ≥9.8 | ≤2.4 | ≥260 | ≥8 | ≥65 |
| AgSnO2 (8) | 92 | ≥9.9 | ≤2.3 | ≥250 | ≥17 | ≥70 |
| AgSnO2 (10) | 90 | ≥9.8 | ≤2.3 | ≥250 | ≥15 | ≥75 |
| AgSnO2 (12) | 88 | ≥9.7 | ≤2.4 | ≥260 | ≥12 | ≥80 |
| AgSnO2 (5) In2O3 (3) | 92 | ≥9.9 | ≤2.3 | ≥250 | ≥17 | ≥75 |
| AgSnO2 (5) In2O3 (4) | 90 | ≥9.8 | ≤2.4 | ≥250 | ≥17 | ≥80 |
| AgSnO2 (5) In2O3 (4) | 88 | ≥9.7 | ≤2.5 | ≥260 | ≥12 | ≥85 |
Babban Tsari:
narkewa
extrusion
zafi mirgina
mirgina sanyi
Ana dubawa shiryawa
saman jiyya
Na ciki oxidized
yin hatimi
Babban Aikace-aikacen